| Standard
Grades |
|
| The oxygen barrier properties
of Soarnol depend on ethylene content and humidity. The most suitable
grade for a given purpose can be determined according to application
and manufacturing process. Please contact
us for suitable recommendations. |
|
| |
|
D2908 |
DT2904R |
DC3212 |
DC3203F |
E3808 |
ET3803 |
A4412 |
AT4403 |
Ethylene
content |
mol% |
29 |
32 |
38 |
44 |
| Density |
g/cm3 |
1.21 |
1.19 |
1.17 |
1.14 |
| Melting point *1 |
deg
C |
188 |
183 |
173 |
164 |
| Crystallization temp. *1 |
deg
C |
163 |
160 |
152 |
144 |
| Glass transition temp. *1 |
deg
C |
62 |
61 |
58 |
55 |
| MFR *2 |
g
/10min |
8 |
3.8 |
12 |
3.2 |
8 |
3.2 |
12 |
3.5 |
Apparent
melt
viscosity *3 |
210degC
poise |
9000 |
24000 |
5500 |
24000 |
9000 |
24000 |
5500 |
20000 |
210degC
Pa s |
900 |
2400 |
550 |
2400 |
900 |
2400 |
550 |
2000 |
230degC
poise |
5000 |
13000 |
2500 |
13000 |
5000 |
12000 |
2500 |
10000 |
230degC
Pas |
500 |
1300 |
250 |
1300 |
500 |
1200 |
250 |
1000 |
| OTR *4 |
cc20 m
/m2dayatm |
0.4 |
0.5 |
0.7 |
1.5 |
cm320
m/m2
24hrsMPa |
4 |
5 |
7 |
15 |
Manufacturing
process |
Blown
film |
|
 |
|
|
|
|
|
|
Cast
film |
|
|
|
|
|
|
|
|
| Sheet |
|
|
|
|
|
|
|
|
| Bottle |
|
|
|
|
|
|
|
|
| Pipe |
|
|
|
|
|
|
|
|
|
|
|
*1 Measured with DSC.
*2 210deg C(410deg F), 230deg C(446deg F)
*3 Measured with melt flow tester which has 1mm *10mmL nozzle and
490N{50kgf}load.
*4 20deg C*65%RH The data in the table are in house standards and
not guaranteed values. |
|
| |
| Specialty
Grades, others |
| |
|
 |
Lower ethylene content grade: V2504R |
 |
|
Higher ethylene content grade: H4815B |
|
|
Thermoforming grades for
PE, PS or PP structure: BX6304B TF2905B |
|
|
|
Flex-crack resistance grade:
ST1304B |
|
|
|
Retortable grade: SG539B |
|
|
|
Pipe grades: D2908H4 DC3205HB |
|
|
Regrind agent for (PE, PS or PP/EVOH)
system: RG100 |
|
| |
|
|
| If you want other information
on specialty materials, please contact
us. |
|
|
|
 |
| |
|